Brush Way High Viscosity Tin Cure Silicone Large Sculpture Statue Mould RTV2 Silicone Rubber
Silicone rubber MCSIL-B230 is a two-component material, consisting of Part A base silicone and Part B MCSIL-CA30, cures at room temperature by a condensation reaction.
APPLICATIONS
MC RTV-2 mold making silicone rubber are suited for reproduction of cement molding, concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds, etc.
FEATURES
1.Capture fine details
2.Medium hardness
3.High tear and tensile strength
4.Easy de-mould from complex replica parts
5.Acid and alkali-resistance
6.Low linear shrinkage
Technical Data
| Item No. | Properties before curing | Curing |
| Part A | Part B | Part A+ Part B | Pot life at 250C | De-molding Time at 25℃ |
| Appearance | Appearance | Ratio | Viscosity |
| MCSIL-B230 | White | Clear | 100:2 | 30000±20000 cps | 15-20 mins | 2-4hours |
| Properties after curing 24 hours |
| Hardness Shore A | Tear strength | Tensile Strength | Elongation break (%) | Linear Shrinkage |
| 28-30 | 28 N/mm | 3.8 Mpa | 450-480 | ≤0.3% |
Silicone Base and Curing Agent Mixture (100:2 by weight) in 25 C(77F) testing
How to make the silicone mold?
Cleaning
The surface of the original should be clean and free of loose material. If your products with thin flower patterns, and especially with porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.
Mixing
Please weight 100 Part A base and 2 parts of Curing Agent in a clean container.Thoroughly stir Part A base silicone before use, as filler separation may occur upon prolonged storage. Mixing Part A and Part B evenly until the CA30 completely dispersed in the base. Hand or mechanical mixing can be used, but do not for an extended period of time or allow the temperature to exceed 35C (95F). Mix suitably small quantities to ensure thorough mixing of base and curing agent.
It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum,the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should
be chosen.
Pouring
Pour the mixed Part A base silicone and part B the curing agent as soon as possible onto the original, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.
Certificates
Package:
Part A base silicone: 5kg, 20kg/drum, 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 250g, 800g/bottle, 1kg/bottle
STORAGE
When stored at or below 30 C (85F) in the original unopened containers, silicone base and CA30 Curing agent have a usable life of 12 months from the date of production. After 12 months stock, please use the Stir to mixing the Part A silicone for some mins, then the silicone can be use again, no influence for other performances.
Note:
Silicone MCSIL series is an industrial product and must not be used in food contact and human skin molding applications.
Product Tags:
|
|